Cytotoxicity Assessment and Indentation Size Effect of Low-Cost Experimental Implant Alloys.

Authors

Nompumelelo V Nkosi, Divesha Essa, Amogelang C Moalodi, Johnson Lawal, Yahya Choonara, Desmond Klenam, Michael O Bodunrin

Published in

ACS materials Au. Volume 6. Issue 4. Pages 808-819. Jul 08, 2026. Epub Apr 09, 2026.

Abstract

The development of affordable lightweight alloys with a combination of high mechanical strength and excellent biocompatibility is crucial for next-generation biomedical implants, particularly for middle- and low-income classes. This study investigates the relationship between processing, microscale mechanical behavior, and cytotoxicity of experimental titanium alloys (Ti-3Fe, Ti-4.5Al-1 V-3Fe, and Ti-6Al-1 V-3Fe) and a low-density stainless-steel (LDSS) alloy (Fe-20Mn-7Al-1C-3Cr-3Cu-3Mo), produced via casting and sintering. Their performance was benchmarked against those of commercial Ti-6Al-4 V and 316L stainless steel. Micro- and macro-indentation tests were conducted to evaluate the indentation size effect (ISE), and the Nix-Gao model was applied to quantify strain-gradient plasticity through the estimation of statistically stored dislocation (SSD) and geometrically necessary dislocation (GND) densities. In parallel, in vitro cytotoxicity was evaluated using NIH-3T3 fibroblast cells following the ISO 10993-5 guidelines. The experimental titanium alloys exhibited pronounced ISE behavior and the highest GND densities, indicating enhanced resistance to plastic deformation at the microscale compared to the LDSS alloys. Cytotoxicity results showed excellent biocompatibility for Ti-6Al-4 V and 316L and good compatibility for the experimental Ti-Fe alloys, with cell viability exceeding 70% at 100% extract concentration. In contrast, the LDSS alloys showed the lowest cell viability, with both the as-cast and sintered LDSS having a cell viability of less than 70%, thereby necessitating a detailed corrosion performance evaluation and further optimization. This performance was correlated with high Mn dissolution detected in the extract medium after the cytotoxicity assessment. The results demonstrate that experimental titanium alloys provide a promising pathway toward lightweight biomedical implant materials that combine microscale strengthening with acceptable biocompatibility.

PMID:
42434470
Bibliographic data and abstract were imported from PubMed on 11 Jul 2026.

Read full publication at:
Please sign in to see all details.

Stats

1-terrible, 9-excellent. How would you rate this publication? Sign in in to submit your rating.

Post a comment

You need to be signed in to post comments. You can sign in here.

Comments

There are no comments yet.