Boron Doping-Induced Lattice Strain Engineering in Cobalt Diselenide: Regulating Cobalt Spin States for Enhanced Oxygen Evolution Reaction.

Authors

Gangbiao Li, Hongfu Leng, Yu Shuai, Shucheng Liu, Yi Liu

Published in

ChemSusChem. Volume 19. Issue 19. Pages e71120. Oct 14, 2026.

Abstract

Spin polarization is a promising strategy for the oxygen evolution reaction (OER) due to the spin-dependent behaviors of intermediates, but its application in transition metal chalcogenides for anion-exchange membrane water electrolyzers (AEMWE) remains rarely reported. Here, density functional theory calculations reveal that partial substitution of selenium (Se) by boron (B) in cobalt diselenide (CoSe₂) induces lattice contraction strain, reducing the spin polarization degree of cobalt (Co) and triggering a high-spin to low-spin transition. Experimental results confirm the presence of compressive strain and enhanced catalytic performance in B-doped CoSe₂. Notably, the B2-CoSe₂ sample, featuring a lattice strain of -0.27%, achieves a current density of 50 mA cm^-2 at an overpotential of only 367 mV in 1 M KOH-35 mV lower than that of pristine CoSe₂. When applied to an AEMWE, this catalyst requires only 2.05 V to achieve a current density of 1 A cm^-2 and exhibits exceptional stability over 120 h at 25 °C in 1 M KOH electrolyte, outperforming commercial RuO₂. Collectively, these findings demonstrate that B-doping-induced lattice contraction strain plays a critical role in modulating the spin polarization and spin state of Co, thereby providing a new paradigm for designing OER catalysts through lattice strain engineering.

PMID:
42811954
Bibliographic data and abstract were imported from PubMed on 30 Sep 2026.

Read full publication at:
Please sign in to see all details.

Stats

1-terrible, 9-excellent. How would you rate this publication? Sign in in to submit your rating.

Post a comment

You need to be signed in to post comments. You can sign in here.

Comments

There are no comments yet.