Effect of Filler Conductive Threshold on Cathodic Protection and Anticorrosion Mechanism of Zinc-rich Epoxy Coatings.

Authors

Yu Wang, Yukang Sun, Xiaolong Zhao, Junfeng Li, Huachao Ma, Kuilin Lv

Published in

ACS applied materials & interfaces. Oct 20, 2026. Epub Oct 20, 2026.

Abstract

In this study, reduced graphene oxide (rGO) fillers with electrical conductivities spanning nearly five orders of magnitude (4.2 × 10-4 - 20.58 S/cm) were prepared by hydrothermal reduction and incorporated at a fixed loading of 0.5 wt % into zinc-rich epoxy coatings containing 50 wt % zinc powder. The influence of the reduction-dependent rGO state on coating structure, interfacial properties, cathodic protection, and corrosion resistance was systematically evaluated. A non-monotonic conductivity-performance relationship was observed, with rGO160 (1.62 S/cm) showing the best overall protection under the present formulation. XPS and FTIR revealed that rGO160 retained an intermediate surface polarity, while cross-sectional SEM and mechanical tests indicated a dense coating structure, reduced interfacial defects, and the highest pull-off adhesion strength (∼6.4 MPa). KPFM further showed a comparatively uniform contact-potential-difference distribution. After 30 days of immersion, the MZrZE-rGO160 coating retained the highest low-frequency impedance modulus (|Z|0.01Hz ≈ 4 × 107 Ω·cm2) and exhibited the lowest relative corrosion propagation after 300 h of salt-spray exposure. DFT calculations showed comparatively less favorable H2O and O2 adsorption on the idealized rGO160 surface (+0.03 and +0.61 eV, respectively), serving as supplementary thermodynamic descriptors rather than direct kinetic evidence. The results demonstrate that the optimum protection arises from the coupled balance of conductivity, surface chemistry, sheet dispersion/restacking, conductive-network connectivity, and coating integrity. Accordingly, 1.62 S cm-1 should be regarded as a formulation-dependent optimum among the investigated rGO fillers rather than a universal conductivity threshold.

PMID:
42896838
Bibliographic data and abstract were imported from PubMed on 20 Oct 2026.

Read full publication at:
Please sign in to see all details.

Stats

1-terrible, 9-excellent. How would you rate this publication? Sign in in to submit your rating.

Post a comment

You need to be signed in to post comments. You can sign in here.

Comments

There are no comments yet.