Authors
Wei Zi, Hehe Huang, Xiaoman Lu, Weiying Mao, Zhaolei Zhang, Lijing Pi, Xiaoli Liu, Kailiang Wang, Yi You, Junqin You, Peishu Yang, Zhenyu Xiao, Jiangfeng Liu, Youchao Tu
Published in
Waste management & research : the journal of the International Solid Wastes and Public Cleansing Association, ISWA. Pages 734242X261489146. Nov 13, 2026. Epub Nov 13, 2026.
Abstract
Developing an eco-friendly route for resource recovery from end-of-life (EOL) crystalline silicon photovoltaic (PV) modules is in high demand. Herein, an automated pilot-scale disassembly line was constructed to mechanically separate backsheets, glass, and ethylene-vinyl acetate (EVA) encapsulant with embedded silicon cells and solder ribbons from EOL PV modules. This prevents backsheets and glass from entering subsequent pyrolysis, inhibits fluorinated gas generation, and reduces energy consumption. The thermal behavior of EVA was analyzed by TG-DSC in air. Subsequently, approximately 2 kg of peeled EVA encapsulant was pyrolyzed in a pilot-scale furnace under different airflow rates to achieve complete removal of the encapsulant, yielding clean and bright crushed silicon cells and solder ribbons. Scanning electron microscope and energy-dispersive X-ray spectroscopy analyses show that airflow rate significantly impacts residual carbon content on silicon cell surfaces; surface carbon content drops from 18.59 wt% to 4.92 wt% when airflow rate increases from 10 to 40 L/min. The results verify that the integrated mechanical peeling-pyrolysis process is promising for large-scale green recycling of EOL PV modules.
PMID:
43023527
Bibliographic data and abstract were imported from PubMed on 13 Nov 2026.
Read full publication at:
Please sign in
to see all details.
Advertisement
Stats
- Recommendations n/a n/a positive of 0 vote(s)
- Views 6
- Comments 0